Posted on May 25, 2017 by dean
Q: I’m using zirconium fasteners in a sulfuric acid process but they are showing corrosion. I’m not sure why as I’m well below boiling and only using 40% concentration. There may be some downstream contaminants, but not much. Any ideas? A: It is most likely the contaminants that are causing … Continue reading →
Posted in Application, Corrosion Resistance, FAQs, High Temperature Resistance, Material, Specialty Metal Fasteners, Technical Questions | Tagged Alloy 625, Alloy C22, Alloy C276, C22, C276, Corrosion, corrosion resistance, Ferric chlorides, H2SO4, Hastelloy, Hastelloy C22, Hastelloy C276, Inconel, Inconel 625, oxidizers, oxidizing media, Sulfuric Acid, tantalum, Zirconium | Leave a comment
Posted on May 24, 2017 by dean
Q: I’m running a steam surface condenser which is installed on a steam turbine in a thermal power station. I’m using sea water that could be contaminated with chemical pollutants cooling water side of the condenser. Any ideas on a good fastener for the tubes and water boxes? A: Duplex 2205 … Continue reading →
Posted in Application, Corrosion Resistance, FAQs, High Temperature Resistance, Specialty Metal Fasteners, Technical Questions | Tagged AL6XN, Alloy 2205, chloride corrosion, Corrosion, Crevice Corrosion, Duplex, Duplex 2205, High Temperature, pitting corrosion, salt water corrosion, Steam condenser, steam surface condenser, Stress Corrosion Cracking | Leave a comment
Posted on May 22, 2017 by dean
Q: I’m using hydrogen fluoride used in a manufacturing process to make refrigerants. I know it’s very corrosive and have tried both hastelloy and inconel fasteners, which I thought were super corrosion resistant. What am I doing wrong because the acid is still eating them? Should I try Tantalum? A: … Continue reading →
Posted on May 20, 2017 by dean
Q: I’m working on a on a geothermal energy drilling project. Carbon steel we’re currently using to bolt drilling components is failing from corrosion. We have corrosive an environment with high levels of sulfur and salt, as well as temperatures to 260C. Any suggestions? A: Super Duplex 2507 is often used … Continue reading →
Posted in Application, Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged Alloy 2507, Crevice Corrosion, Duplex, Duplex 2507, Geothermal drilling, geothermal exploration, geothermal well, Hastelloy, Inconel, pitting corrosion, SCC, Stress Corrosion Cracking, Super Duplex, Super Duplex 2507 | Leave a comment
Posted on May 18, 2017 by dean
q: What bolting material should be used with Inconel 625 flanges? We used ASTM A193 Gr B7 however noticing some corrosion issues. A: This is a very common problem but to answer it accurately, it depends on the environment that your flanges see and also to a certain extent what … Continue reading →
Posted in Application, Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged Alloy 625, Alloy 718, B7, Corrosion, flange, Galvanic Corrosion, Inconel, Inconel 625, Inconel 718 | Leave a comment
Posted on May 11, 2017 by dean
They rhyme, are both used in extreme environments, and are both nickel metal alloys, but Monel and Inconel are actually very different. But how? Let’s start with basic chemistry. Monel is a nickel-copper alloy and Inconel is a nickel-chromium alloy. So what does that mean for your extreme application? We … Continue reading →
Posted in Application, Blog, Corrosion Resistance, High Strength, High Temperature Resistance, Specialty Metal Fasteners | Tagged Alloy 400, Alloy 625, Corrosion, hastelloy C2000, High Temperature, Hydrofluoric acid, Inconel, Inconel 625, Monel, Monel 400, saltwater corrosion, sea water corrosion | 1 Comment
Posted on May 2, 2017 by dean
Q: I’m running a semiconductor wet chemical etching process that utilizes 85 % phosphoric acid at around 150-160°C. I need a material that can withstand this process. Super Duplex hex bolts are not cutting it. A: At that particular concentration and temperature high performance nickel alloys like Hastelloy C276 bolts … Continue reading →
Posted on May 1, 2017 by dean
Q: I have a waste water purifying situation where I’m using chlorine to treat the water. In addition to the acidic solution produced the fastener will also experience high loads, so I’m also concerned with stress corrosion cracking. Currently Super Duplex 2507 is not doing the job. Any recommendations on … Continue reading →