Tag Archives: Alloy 330 fasteners for high temperature oxidation resistance

Oxidation Resistant A286 and Alloy 330 Bolt

Posted on April 6, 2021 by Kathleen

Q: I was reading that high temperatures will accelerate the rusting of metal bolts. Is there a material that can prevent this. I’m using the screws at 1300F intermittently. A: What you are looking for is an oxidation resistant bolt. When a metal oxidizes it is attacked by oxygen which … Continue reading →

Posted in Application, FAQs, High Temperature Resistance, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , , , , , , , , , , , , , , , , , | Leave a comment

Oxidation Resistance for Heat Treating

Posted on February 18, 2021 by Kathleen

Q: I am interested in 1/4″ x 2 1/2′ bolts and nuts that can resist oxidation up to 2000F. The application they are needed for would be to hold together a steel frame meant to hold tool steel in position preventing distortion during the heat treating process. I would like … Continue reading →

Posted in Application, FAQs, High Temperature Resistance, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , | Leave a comment

Inconel 600 Bolts & Alloy 330 Bolts for High Temperature Oxidation

Posted on October 19, 2020 by Kathleen

Q: I have an application that requires high temperature oxidation resistance up to about 2000F. Any suggestions? A: For these conditions there are two options I would suggest. You could try Inconel 600 bolts which are usable to 2000F. They offer excellent carburization and oxidation resistance. Since your process is … Continue reading →

Posted in Application, FAQs, High Temperature Resistance, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , | Leave a comment