Tag Archives: Duplex 2507
Posted on November 15, 2017 by dean
Q: I have a high strength application that requires resistance to damp salt air and occasional sea splash, I’m using Monel 400 but it’s not holding up the the 75ksi of yield I need. Lots of broken bolts? Is is corrosion or strength? Thoughts? A: Your issue isn’t the corrosion. … Continue reading →
Posted in Application, Corrosion Resistance, FAQs, High Strength, Material, Specialty Metal Fasteners, Technical Questions | Tagged Alloy 400, Alloy K500, Corrosion, Duplex 2507, Duplex Steel, Monel, Monel 400, Monel K500, salt water, salt water corrosion, sea water corrosion, seawater | Leave a comment
Posted on August 16, 2017 by dean
Q: I have down hole application containing sour gas and high chloride levels. The temperature the bolts are exposed to is around 150F and I’m having trouble with cracking. I tried Super Duplex 2507 but am still having issues. Any ideas? A: Super Duplex 2507 does provide good resistance to … Continue reading →
Posted on July 5, 2017 by dean
Q: I’m using sodium hypochlorite to control slime and bacteria formation in a power plant water system. It’s in about a 15% solution. I tried using Duplex fasteners thinking they are good with chlorides but I’m having corrosion issues. Any suggestions? A: I think the problem you have is the fact … Continue reading →
Posted on June 6, 2017 by dean
Q: I’m working on a structural project that not submerged in salt water but exposed to moist salt air. I’m not only concerned about the supports having fasteners that won’t corrode but also having a fastener that is high strength. Any suggestions. A: Though I don’t know the specific strength … Continue reading →
Posted in Application, FAQs, High Strength, Material, Specialty Metal Fasteners, Technical Questions | Tagged Duplex, Duplex 2205, Duplex 2507, Duplex Steel | Leave a comment
Posted on May 20, 2017 by dean
Q: I’m working on a on a geothermal energy drilling project. Carbon steel we’re currently using to bolt drilling components is failing from corrosion. We have corrosive an environment with high levels of sulfur and salt, as well as temperatures to 260C. Any suggestions? A: Super Duplex 2507 is often used … Continue reading →
Posted in Application, Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged Alloy 2507, Crevice Corrosion, Duplex, Duplex 2507, Geothermal drilling, geothermal exploration, geothermal well, Hastelloy, Inconel, pitting corrosion, SCC, Stress Corrosion Cracking, Super Duplex, Super Duplex 2507 | Leave a comment