Tag Archives: high temperature fasteners
Posted on April 15, 2022 by Kathleen
Q: I don’t see 316 on your sight but would you know if 316H material can be useed at 1500F? A: I believe 316H will survive 1500F without significant oxidation. However, please be aware, at that temperature, the material will lose a significant % of its strength. The material already … Continue reading →
Posted in Application, FAQs, High Temperature Resistance, Material, Specialty Metal Fasteners, Technical Questions | Tagged 316 at high temperatures, 316 bolts at high temperatures, 316H bolts at 1500f, 316H screws at 1500F, High Temperature, High temperature bolts, high temperature fasteners, High temperature screws | Leave a comment
Posted on March 8, 2018 by dean
Q: I have a need for a high temperature bolts that will be used in continuous heat at about 1000F. Any suggestions? Also, will fluctuations in temperature cause breakage? A: One of the best materials for long-term continual exposure to high temperatures are Incoloy bolts. The Incoloy 800 series will … Continue reading →
Posted in Application, FAQs, High Temperature Resistance, Specialty Metal Fasteners, Technical Questions | Tagged Bolts for 1000F, Fasteners for 1000F, Fasteners for high temperature, High temperature bolts, high temperature fasteners, High temperature screws, Incoloy bolts for high temperature, Incoloy fasteners for high temperature | Leave a comment