Tag Archives: monel fasteners for saltwater corrosion

Q: I’ve been using Monel 400 bolts for a coastal operation that is built in polluted, stagnant saltwater. I’m been having some slight corrosion – nothing drastic, but wanted to check if there was another material that would last longer. A: For this situation I would suggest titanium bolts. Titanium … Continue reading

Posted in Application, Corrosion Resistance, FAQs, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , , , , , , , , , , , , , | Leave a comment

Q: We are installing bolts into a refinery wharf.  After doing a test run on a few A316 stainless steel bolts, they came back heavily corroded. Do you have an coating that can be used for salt water applications that would prevent this? Or do can you advise on another … Continue reading

Posted in Application, Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , , , , | Leave a comment