Q: What heat treatment would you recommend for 17-4PH exposed to salt water? Can I use H900?
A: H900 is susceptible to chloride stress corrosion cracking. 17-4 with salt exposure should be H1025 or higher. And, best practice it to use the highest heat treat temp that works for an application.