Tag Archives: Monel 400

Monel Bolts for Saltwater Wharf

Posted on March 27, 2020 by dean

Q: We are installing bolts into a refinery wharf.  After doing a test run on a few A316 stainless steel bolts, they came back heavily corroded. Do you have an coating that can be used for salt water applications that would prevent this? Or do can you advise on another … Continue reading →

Posted in Application, Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , , , , | Leave a comment

Duplex 2507 bolts for high strength application in salt air

Posted on November 15, 2017 by dean

Q: I have a high strength application that requires resistance to damp salt air and occasional sea splash, I’m using Monel 400 but it’s not holding up the the 75ksi of yield I need. Lots of broken bolts? Is is corrosion or  strength? Thoughts? A: Your issue isn’t the corrosion. … Continue reading →

Posted in Application, Corrosion Resistance, FAQs, High Strength, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , | Leave a comment

AL6XN vs Monel bolts for salt water and marine use

Posted on November 14, 2017 by dean

Q: Is AL6XN a steel or nickel alloy? Trying to figure out if it would perform as well as Monel in seawater. A: To answer your first question, AL6XN bolts are actually both a nickel and a steel alloy. AL6XN is often described as a high nickel content stainless alloy. Though … Continue reading →

Posted in Application, Corrosion Resistance, FAQs, Material, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , , , , , | Leave a comment

Nickel Alloys Part 1: Moderate Corrosion

Posted on November 2, 2017 by dean

Nickel alloys are a special class of metals containing high levels of nickel (often greater than 20%). They play a key role in industry for their unique combination of high strength, corrosion resistance to harsh acids (like hydrochloric and sulfuric) and high temperature stability. This two-part newsletter will help summarize the distinct benefits of the … Continue reading →

Posted in Application, Blog, Corrosion Resistance, Material, Specialty Metal Fasteners | Tagged , , , , , , , , , , , , , , , , | Leave a comment

Screws for high velocity salt water with debris

Posted on July 10, 2017 by dean

Q: I have a salt water environment with high velocities and a lot of debris including sand, dirt and particles. Because of the amount of debris, I’m concerned about what material would work best. A: Both Monel and Titanium can be good choices in this situation. Both perform extremely well … Continue reading →

Posted in Application, Corrosion Resistance, Specialty Metal Fasteners | Tagged , , , , , , , , , , , , , | Leave a comment

Tantalum vs Monel fasteners in hydrogen fluoride

Posted on May 22, 2017 by dean

Q: I’m using hydrogen fluoride used in a manufacturing process to make refrigerants. I know it’s very corrosive and have tried both hastelloy and inconel fasteners, which I thought were super corrosion resistant. What am I doing wrong because the acid is still eating them? Should I try Tantalum? A: … Continue reading →

Posted in Corrosion Resistance, FAQs, Specialty Metal Fasteners, Technical Questions | Tagged , , , , , , , , , , | Leave a comment

Inconel bolts vs. Monel bolts. What’s the difference? Which is better?

Posted on May 11, 2017 by dean

inconel-monel-chart-copyThey rhyme, are both used in extreme environments, and are both nickel metal alloys, but Monel and Inconel are actually very different. But how? Let’s start with basic chemistry. Monel is a nickel-copper alloy and Inconel is a nickel-chromium alloy. So what does that mean for your extreme application? We … Continue reading →

Posted in Application, Blog, Corrosion Resistance, High Strength, High Temperature Resistance, Specialty Metal Fasteners | Tagged , , , , , , , , , , , | 1 Comment

Sea Water Corrosion: Monel, AL-6XN & Titanium to the Rescue

Posted on September 21, 2016 by dean

With over 30% of marine equipment failures being the result of marine corrosion, the subsequent costs have added up; now seawater corrosion costs are estimated at 4 % of the GNP. Unfortunately, sea water is not a simple medium because it is chemically and biologically active, which can have an … Continue reading →

Posted in Blog | Tagged , , , , | Leave a comment