Q:We have an anodizing process that sends low voltage current through aluminum bars. We have been using 316 stainless bolts, but over time the electricity heats the bolts up red hot, then we lose clamping force. The tanks contain a solution of 15% sulfuric acid, so there is some corrosion … Continue reading →