Tag Archives: Zirconium
Posted on May 25, 2017 by dean
Q: I’m using zirconium fasteners in a sulfuric acid process but they are showing corrosion. I’m not sure why as I’m well below boiling and only using 40% concentration. There may be some downstream contaminants, but not much. Any ideas? A: It is most likely the contaminants that are causing … Continue reading →
Posted in Application, Corrosion Resistance, FAQs, High Temperature Resistance, Material, Specialty Metal Fasteners, Technical Questions | Tagged Alloy 625, Alloy C22, Alloy C276, C22, C276, Corrosion, corrosion resistance, Ferric chlorides, H2SO4, Hastelloy, Hastelloy C22, Hastelloy C276, Inconel, Inconel 625, oxidizers, oxidizing media, Sulfuric Acid, tantalum, Zirconium | Leave a comment
Posted on May 2, 2017 by dean
Q: I’m running a semiconductor wet chemical etching process that utilizes 85 % phosphoric acid at around 150-160°C. I need a material that can withstand this process. Super Duplex hex bolts are not cutting it. A: At that particular concentration and temperature high performance nickel alloys like Hastelloy C276 bolts … Continue reading →
Posted on February 8, 2017 by dean
Q: What is the difference between Zirconia and Zirconium? A: Zirconia is a ceramic made from ZrO2 and Zirconium (Zr) is a refractory metal element found on the periodic table. So while Zirconia is made from Zirconium they are VERY different.